PVC Credit Card Sheet

The material supports embossing (raised character printing) and contains no substances that could interfere with or alter magnetic properties. It is compatible with magnetic stripe attachment or chip embedding. Primarily used in sectors including finance, transportation, postal and telecommunications, education, as well as food, beverage, and entertainment services. Suitable for producing bank credit cards, debit cards, securities cards, and similar applications.

PVC Bank credit card base materials

Bank card introduction

1 Specification: The size error of the thickness, width and length of the standard credit card shall comply with the provisions of Table 1

project	specifications	allowable deviation
thickness	0.15-0.25	±0.0075
	0.25-0.50	Soil 0.01
	0.51-0.70	±0.015
width	≥250	±1
length	≤1000	±1
Positive square degree	1m×1m	1.2

2 Appearance: The appearance indicators of the standard credit card shall meet the provisions of Table 2

project		metric
surface		4～15%
Gloss degree of% ≤		4～25%
fluorescence		Non-fluorescent products do not glow under UV light
chromatic aberration △E≤		1
harshness	Ra um	0.7-1.5
	Rz um	5-9
impurity	Particle size: 0.3mm-0.5mm	10 ² / m
	Particle size of> 0.5mm	not allow

3. Mechanical performance: The mechanical performance index of the standard credit card shall meet the provisions of Table 3

project		metric
The tensile strength of the Mpa≥		40
Falling ball impact breaking rate% ≤		35
The Vica softening temperature ℃		73±2
density g/cm³		1.38±0.05
Surface tenine / cm ²≥		≥38
Heating shrinkage% 140℃×10min	0.15mm-0.25mm≤	\|8\|
	0.26mm-0.5.mm≤	\|5\|
	0.51mm-0.7.mm≤	\|3\|